Aacsr Phlox-75 Aluminiumlegierung Kernstahl Verstärkt


                                 Aacsr Phlox-75 Aluminiumlegierung Kernstahl Verstärkt

Basis Info

Modell Nr..
AACSR Phlox-75

Art
Blank

Leitertyp
Stranded

Anwendung
Oben

Leitermaterial
Aluminium

Isoliermaterial
Blank

Material Form
Runddraht

Bescheinigung
ISO9001 ,
CCC

Zusätzliche Informationen.

Warenzeichen
Huatong

Verpackung
Wood Drum or Steel- Wood Drum

Standard
Steel wire and Alloy 6201

Herkunft
China

HS-Code
7614100000

Produktionskapazität
5000ton/Month

Produktbeschreibung

AACSR Phlox-75 Aluminium alloy core steel reinforced 

Construction:
The AACSR conductors are also suitable for use in all practical transmission towers,and other structures. Application range from extra high voltage(EHV) transmission lines to sub-service spans at distribution or utilization voltages on private premises as like as ACSR.
AACSR(Aluminum Alloy Conductor Steel Reinforced) has also a long service record because of its economy ,dependability, and strength to weight ratio. The combined light weight and high conductivity of aluminum with strength of the steel cores enable higher tensions ,less sag,and longer spans than any alternative as like as ACSR.
Compared with ACSR ,the tensile strength of aluminum conductor is more strong .

Bare Conductor Types
(1) all aluminum conductor (AAC)
(2) all aluminum alloy conductor(AAAC)
(3) aluminum conductor steel reinforced (ACSR)
(4) aluminium alloy conductor steel reinforced (AACSR)
(5) aluminum conductor aluminum clad steel reinforced(ACSR/AW)
(6)rear earth aluminum conductor steel reinforced(ACSR/RE)
(7)aluminum conductor aluminum alloy reinforced(ACAR)

IF YOUR HAVE ANY INTERESTED PRODUCTS, PLS FEEL FREE TO CONTACT OUR SALES TEAM.
We are the professinal factory who offer your best support!

Aluminum Alloy 6201 wires and the steel cores are concentrically stranded and wrapped helically around a central wire. The additional corrosion protection is available through the application of grease to the cores or infusion of the complete cable with grease.
 

No. Item of test Unite Requirement Test result Judgment
1 Structure Size
1.1 Aluminum wire
-Number
-Diameter
 
/
mm
 
12
2.25±0.03
 
12
  2.225~2.260
Qualified
1.2 Direction of cable / right right Qualified
1.3 Diameter of cable mm 11.25 11.25 Qualified
1.4 Weight:
-Conductor
-Grease
Kg/km  
348
4.84
 
350
7
Qualified
1.5 Al alloy lay ratio / 10-14     12.95 Qualified
1.6 Steel wire
-Number
-Diameter
 
/
mm
 
7
2.25±0.03
 
7
2.225~2.270
Qualified
1.7 Direction of steel wire / left left Qualified
1.8 Diameter of steel core mm 6.75 6.76 Qualified
1.9 Lay ratio of outer steel layer / 16-22 19.13 Qualified
2 Appearance / Smooth and equivalent Smooth and equivalent Qualified
3 Inertness / Evenly and Closely Evenly and Closely Qualified
4 The properties of aluminum alloy wire
4.1 Tensile strength MPa ≥295 310~325 Qualified
4.2 Wrapping / 1d winds 8 circles,returns 6 circles,once closely wind No breaking Qualified
4.3 D.C.resistance at 20ºC nΩ·m ≤32.53 31.875~32.506 Qualified
5 The properties of steel wire
5.1 Tensile strength MPa ≥1462 1534~1622 Qualified
5.2 Minium stress of steel wire at 1 percent extension MPa ≥1410 1463 Qualified
5.3 Elongation in 250mm length on breaking % ≥3.0 4.0 Qualified
5.4 Torsion(L=100d) pcs/360° ≥14 23~28 Qualified
5.5 wrapping 1D No breaking No breaking Qualified
5.6 Mass of zinc coating g/ m2 ≥230 258~275 Qualified
5.7 Adherence of zinc coating 4d/8turns The zinc coating shall not crack or flake to such an extent that any zinc can be removed by rubbing with bare fingers. Qualified Qualified
 
 
6
 
 
Length per drum meter         4593 4598 Qualified
4680 4690 Qualified
4514 4522 Qualified

 

 

Nominal
Cross Section
Alloy Cross Section Steel Cross Section Number
of Alloy
Wires
Diameter
of Alloy
Wires
Number
of Steel
Wires
Diameter
of Steel
Wires
Overall
Diameter
Linear
Mass
Rated
Tensile
Strength
Max.D.C. Resistance
at 20ºC
mm² mm² mm² mm mm mm kg/km daN Ω/km
163 140 23 26 2.62 7 2.04 16.6 560 7500 0.24
173 140 33 30 2.44 7 2.44 17.1 650 8740 0.24
186 160 26 26 2.8 7 2.18 17.7 645 8560 0.21
198 160 38 30 2.61 7 2.61 18.3 740 10600 0.21
209 180 29 26 2.97 7 2.31 18.8 725 9510 0.187
222 180 42 30 2.76 7 2.76 19.3 825 11200 0.187
232 200 32 26 3.13 7 2.43 19.8 800 10600 0.168
247 200 47 30 2.91 7 2.91 20.4 920 12400 0.168
260 224 36 26 3.31 7 2.57 21 900 11800 0.15
276 224 52 30 3.08 7 3.08 21.6 1025 13900 0.15
291 250 41 26 3.5 7 2.72 22.2 1010 12900 0.135
308 250 58 30 3.26 7 3.26 22.8 1145 15600 0.135
326 280 46 26 3.7 7 2.88 23.4 1140 14400 0.12
345 280 65 30 3.45 7 3.45 24.2 1280 17100 0.12
367 315 52 26 3.93 7 3.06 24.9 1276 16300 0.107
387 315 72 30 3.66 19 2.2 25.6 1433 19000 0.107
413 355 58 26 4.17 7 3.24 26.4 1433 18300 0.095
436 355 81 30 3.88 19 2.33 27.2 1614 21100 0.095
465 400 65 26 4.43 7 3.45 28.1 1612 20700 0.0842
491 400 91 30 4.12 19 2.47 28.8 1816 23700 0.0842
509 450 59 54 3.26 19 1.98 29.5 1703 21500 0.0748
563 500 63 54 3.43 19 2.06 30.9 1873 22900 0.0673
631 560 71 54 3.63 19 2.18 32.7 2101 25700 0.0601
710 630 80 54 3.85 19 2.31 34.6 2365 28600 0.0534
800 710 90 54 4.09 19 2.45 36.8 2665 32200 0.0474
901 800 101 54 4.34 19 2.6 39 3000 36300 0.042
973 900 73 84 3.69 19 2.21 40.6 3062 35500 0.0374
1081 1000 81 84 3.89 19 2.33 42.8 3395 39100 0.0337
1211 1120 91 84 4.12 19 2.47 45.3 3803 43900 0.03
1352 1250 102 84 4.35 19 2.61 47.8 4250 49000 0.027

 